Abstract:Developing effective and practical electrocatalyst under industrial electrolysis conditions is critical for renewable hydrogen production. Herein, we report the self-supporting NiFe LDH-MoSx integrated electrode for water oxidation under normal alkaline test condition (1 M KOH at 25 °C) and simulated industrial electrolysis conditions (5 M KOH at 65 °C). Such optimized electrode exhibits excellent oxygen evolution reaction (OER) performance with overpotential of 195 and 290 mV at current density of 100 and 400 mA·cm−2 under normal alkaline test condition. Notably, only overpotential of 156 and 201 mV were required to achieve the current density of 100 and 400 mA·cm−2 under simulated industrial electrolysis conditions. No significant degradations were observed after long-term durability tests for both conditions. When using in two-electrode system, the operational voltages of 1.44 and 1.72 V were required to achieve a current density of 10 and 100 mA·cm−2 for the overall water splitting test (NiFe LDH-MoSx/INF || 20% Pt/C). Additionally, the operational voltage of employing NiFe LDH-MoSx/INF as both cathode and anode merely require 1.52 V at 50 mA·cm−2 at simulated industrial electrolysis conditions. Notably, a membrane electrode assembly (MEA) for anion exchange membrane water electrolysis (AEMWEs) using NiFe LDH-MoSx/INF as an anode catalyst exhibited an energy conversion efficiency of 71.8% at current density of 400 mA·cm−2 in 1 M KOH at 60 °C. Further experimental results reveal that sulfurized substrate not only improved the conductivity of NiFe LDH, but also regulated its electronic configurations and atomic composition, leading to the excellent activity. The easy-obtained and cost-effective integrated electrodes are expected to meet the large-scale application of industrial water electrolysis.3D integrated electrode NiFe LDH-MoSx exhibits superior OER performance at both normal alkaline condition and simulated industrial electrolysis conditions (5 M KOH/65 °C) and has the prospect of large-scale application in industrial water electrolysis.

Boosting Electrochemical Water Oxidation on NiFe (oxy) Hydroxides by Constructing Schottky Junction toward Water Electrolysis under Industrial Conditions

High-Density NiMnFe Hydroxide Nanoparticle-Nanosheet Arrays for Industrial-Level Electrochemical Oxygen Evolution Reaction

Construction of an Electrode with Hierarchical Three-Dimensional NiFe-oxyhydroxides by Two-Step Electrodeposition for Large-Current Oxygen Evolution Reaction

Self-supporting NiFe LDH-MoS integrated electrode for highly efficient water splitting at the industrial electrolysis conditions

Schottky Heterojunction Nanosheet Array Achieving High‐Current‐Density Oxygen Evolution for Industrial Water Splitting Electrolyzers

Bimetallic Oxyhydroxide as a High-Performance Water Oxidation Electrocatalyst under Industry-Relevant Conditions

Boosting oxygen evolution reaction by FeNi hydroxide-organic framework electrocatalyst toward alkaline water electrolyzer

Ni-modified FeOOH integrated electrode by self-source corrosion of nickel foam for high-efficiency electrochemical water oxidation

Ultrastable NiFeOOH/NiFe/Ni electrocatalysts prepared by in-situ electro-oxidation for oxygen evolution reaction at large current density

2D NiFe2O4/Ni(OH)2 Heterostructure‐Based Self‐Supporting Electrode With Synergistic Surface/Interfacial Engineering for Efficient Water Electrooxidation

Hybrid Heterostructure Ni3N|NiFeP/FF Self‐Supporting Electrode for High‐Current‐Density Alkaline Water Electrolysis

Efficient Electrocatalytic Oxygen Evolution at Extremely High Current Density over 3D Ultrasmall Zero‐Valent Iron‐Coupled Nickel Sulfide Nanosheets

Boosting Oxygen Evolution Reaction of (Fe,Ni)Ooh via Defect Engineering for Anion Exchange Membrane Water Electrolysis Under Industrial Conditions

Electronic modulation of FeOOH coupled NiFe-LDH for highly efficient alkaline water oxidation at high current density

In-situ synthesis of free-standing FeNi-oxyhydroxide nanosheets as a highly efficient electrocatalyst for water oxidation

Acid-Corrosion-Induced Hollow-Structured NiFe-Layered Double Hydroxide Electrocatalysts for Efficient Water Oxidation

Facilitating interface charge transfer via constructing NiO/NiCo 2 O 4 heterostructure for oxygen evolution reaction under alkaline conditions

One-step electrodeposition of composition-controllable dendritic NiFe alloy electrocatalysts for oxygen evolution reaction

3D-Printed Hierarchically Micro–Nano-structured NiFe Catalysts for the Stable and Efficient Oxygen Evolution Reaction

Ultrafast Room‐Temperature Synthesis of Large‐Scale, Low‐Cost, and Highly Active Ni─Fe Based Electrodes toward Industrialized Seawater Oxidation

In-situ construction of 3D hetero-structured sulfur-doped nanoflower-like FeNi LDH decorated with NiCo Prussian blue analogue cubes as efficient electrocatalysts for boosting oxygen evolution reaction