Abstract:Phosphogypsum is a solid waste produced in the production of wet-process phosphoric acid. The main component is calcium sulfate dihydrate, and its constant calcium activity is very low. It is a very difficult waste to handle. The slag produced in the ironmaking processes of the Jiuquan Iron and Steel Company has high activity and can be mixed with phosphogypsum to prepare backfilling cementitious materials for the backfilling of goaf (see Introduction below) to prevent its subsidence and cracking and subsequent subsidence of the land surface above the goaf. In this paper, an orthogonal test of material strength under different ratios and finenesses was carried out, and the optimal formula of phosphogypsum-based cementitious material was obtained. On this basis, SEM (Scanning Electron Microscope) and XRD (X-ray Diffraction) were used to observe the internal structure of phosphogypsum-based cementitious materials. The results show that: when the content of quicklime is 5.5%–6.0%, the content of phosphogypsum is 30%–33%, the content of NaOH is 1.5%–2.0%, the content of Glauber's salt is 2.5%–3%, the average particle size is 15.88 μm, and grinding aids and an early strengthening agent were added, and in the case of the strengthening agent, the 3-days and 7-days strengths of the filling reached the highest values of 1.58 MPa (mean flexural strength) and 4.1 MPa, respectively. The formation of calcium silicate hydrates gel (C-S-H) and ettringite (AFt) gradually increased with age, and the structure became denser. The ettringite plays the role of interspersed support in the filling body, thereby improving the overall strength. This research provides a theoretical basis and practical reference for the treatment of goaf.

Phosphogypsum-based stone-like structure building material and preparation method thereof

Synthesis of High-Strength and Water-Resistant Phosphogypsum Small Hollow Block

Preparation of high-performance lightweight materials based on the phosphogypsum-inorganic material system

Phosphogypsum-Based Ultra-Low Basicity Cementing Material

A Sustainable Composite Cementitious Material Manufactured by Phosphogypsum Waste

Enhancement of phosphogypsum mechanical block with the addition of iron and aluminum salts

New dawn of solid waste resource treatment: Preparation of high-performance building materials from waste-gypsum by mechanical technology

Mechanical properties and soluble phosphorus solidification mechanism of a novel high amount phosphogypsum-based mortar

Low-Energy Consumption Preparation of Fine Waterproof Cementitious Material with High-Volume Phosphogypsum

Utilization of waste phosphogypsum to prepare non-fired bricks by a novel Hydration–Recrystallization process

Deep removal of phosphorus and synchronous preparation of high-strength gypsum from phosphogypsum by crystal modification in NaCl-HCl solutions

Research on formulation optimization and hydration mechanism of phosphogypsum-based filling cementitious materials

An effective treatment method for phosphogypsum

Harmless disposal of phosphogypsum synergized red mud: Harmful element control and material utilization

Preparation of paper-free and fiber-free plasterboard with high strength using phosphogypsum

An Eco-Friendly Phosphogypsum-Based Cementitious Material: Performance Optimization and Enhancing Mechanisms

Effect of limestone powder on mechanical properties and microstructure of phosphogypsum

Preparation of Foamed Phosphogypsum Lightweight Materials by Incorporating Cementitious Additives

Characteristic pollutant purification analysis of modified phosphogypsum comprehensive utilization

Sustainable Utilization of Phosphogypsum in Multi-Solid Waste Recycled Aggregates: Environmental Impact and Economic Viability